Weldable 63HRC Crmo White Iron Wear Plates for Chute Liner Protection High Impact Toughness

• Customization: Available
• After-sales Service: Spare Parts for Free
• Warranty: 3 Years
• Model NO.: Weldable 63HRC CrMo White iron Wear Plates
• Certification: ISO 9001:2008
• Standard: ASTM
• Surface Treatment: Shot Blast
• Manufacturing Process: Casting
• Material: Cast Iron
• Application: Ore Mining Wear Protection
• Hardness: 700bhn / 63HRC
• Wear Material: Crmo White Iron(Domite)
• Base Material: Mild Steel or Equivalent
• Typical Feature: Extremly Abrasion and Impact Toughness
• Typical Application: Chute Liner, Transfer Point, Liner Protections
• Transport Package: Ply-Wood Crate & Pallet
• Specification: 10~45mm thick, width and lengt varies
• Trademark: Hystertech, OEM
• Origin: China
• HS Code: 84749000
• Production Capacity: 3000 Tons/Year

Product Description

Bimetallic chrome white iron brazed wear plates

 

Material: Chrome white iron wear casting vacuum brazed onto mild steel base.

The smallest thickness for wear material we can make is 6mm.

 

Advantage:

1. Hardness: 63HRC/700BHN. The usage life is at least 2 times higher compared with overlay/hardfacing wear plates, at least 7 times longer than A.R type steels 360/400BHN. The thicker ones such as 20mm above wear, the usage life is much more longer. The wear resistance performance is the same from wear surface to the welding face.

2. Wear surface is very smooth and flat, media is not easy to stick on.

3. It can make with different shapes and sizes.

4. Better cost-efficient. Unit price is about USD5.0~USD7.5 per kilogram.

 

Suitable for use in chutes, hoppers, bins, liners, impact walls, rock boxes and a variety of other applications.  

Very easy to use, no pre or post heating when welding.

In every case, we enable customers to:

• •Reduce downtime due to unscheduled break downs
• •Save on equipment cost & renewal costs
• •Save man hours on maintenance
• •Minimising & eliminating lost production
• •Increase their bottom line by achieving savings in all of the above

Typical Data NumbersWhite Iron Wear Parts

 

• Usage life is 50% greater than that of Ni Hard Irons.
• At least 7 times longer than A.R. type steels 360/400 BHN
• 5 times the wear rate of Manganese Steel
• 3 times the wear rate of Tapco Weld Hardfacing
• 4 times the wear rate of Astralloy-Vulcan
• 16 times the wear rate of Carbon Steel
• 3 times the wear rate of 500 BHN A.R. Plat

Bimetallic White Iron Wear Plate Usage Life is Three Times Higher Than Overlay Wear Plates!!

Applications---Typical applications include the following for the Sugar, Mining, Quarrying, Re-cycling, Aggregate and other Heavy Industries (to name only a few of the countless applications):

• Chute Linings
• Apron Feeder Liners
• Dump& Crusher Hoppers
• Distribution Plates
• Rock Box Liners

• Crusher Chutes/Bars
• Conveyor Transfer Points
• Knife Inserts
• Feeders
• Loaders

• Flop Gates
• Draglines& Shovels
• Hammer Mill Inserts
• Wear Aprons/Pads
• Dump Hoppers & Crusher Hoppers

• Surge Bin& Bucket& Trough Liners
• Rock Box& Hopper Edges/Liners
• Rolling Mill Guides
• Jaw Crusher Check Plates
• Skid Plates

• Skip& Loader& Truck Bed Liners
• Lip& Adaptor Protectors
• Screen Plates
• Drag Line Bucket Liners
• Coal Transfer& Tripper Chutes

Detailed Technical Data:

Material

This Bi-metallic wear resistant product, as a combination of high Chromium cast iron (ASTM A532 15/3CrMo, 700BHN - 63HRc) metallurgically bonded to a mild steel backing plate, obtains both very high abrasion resistance and weldability.

Chemical Composition of White Iron

C	Cr	Mn	Mo	Cu	P	Si	S	B,V,Nb
2.5~3.5%	15~18%	0.5~1.0%	0.5~2.5%	0.5~1.0%	≤0.02%	0.5~1.0%	≤0.02%	0.1~0.5%

Mechanical Property of White Iron
 

1. Tensile Strength: 630 MPa
2. Shearing Strength: 250 MPa
3. Hardness: 63 HRC

Micro-Structure of White Iron


Product Series
Chocky Bars                               Wear Buttons                          Wear Donuts
Standard Wear Bars                 Micro-Ledges                           Wear Plates
Rock Box Liners                        Skid Wear Bars                         Shaped Wear Bars
Wafer Strips                              Grizzly Bars                               Elbow Wear Bars
Shredder Hammer Tips           Knife Edges                               Overlay Wear Plates
 
Applications
Wear Pads                 Jaw Crushers                     Chute Linings              Ore Chutes
Crusher Chutes         Tripper Chutes              Flop Gates                   Bucket Liners
Grizzly Bars                Lip Protectors               Screen Plates              Vibratory Feeders
Floor Liners                Loaders                         Wear Aprons               Knife Inserts
Crusher Bars              Run Out Rolls               Dump Hoppers           Crusher Hoppers


Specifications of Standard Wear Plates

-Better wear resistance performance

-Durable

-Cost effective

-Excellent quality

Notes: Arc studs available as per sizes or drawings provided.


 

Type	Item No.	Size (mm)	Dimension (mm)					N.W. (kg)
			A	B	C	D	E
Standard	WP 200-18	200×200×18	200	200	12	6	18	5.7
	WP 200-20	200×200×20	200	200	14	6	20	6.3
	WP 300A	300×150×20	300	150	14	6	20	7.0
	WP 250	250×250×20	250	250	14	6	20	9.8
	WP 300	300×300×18	300	300	12	6	18	12.7
	WP 300B	300×300×20	300	300	14	6	20	14.1
	WP 305	305×150×24	305	150	18	6	24	8.6
	WP 300C	300×150×25	300	150	19	6	25	8.8
	WP 300D	300×300×24	300	300	19	6	25	17.7
	WP 445	445×445×25	445	445	19	6	25	38.9
	WP 301	301×200×28	301	200	18	10	28	13.2
	WP 294A	294×144×30	294	144	20	10	30	10.2
	WP 294B	294×294×30	294	294	20	10	30	20.4
	WP 300E	300×150×30	300	150	20	10	30	10.6
	WP 300F	300×300×30	300	300	20	10	30	21.2
	WP 372	372×372×28	372	372	20	8	28	30.4
	WP 300G	300×300×50	300	300	40	10	50	35.5
	WP 300H	300×148×50	300	148	40	10	50	17.4
	WP 206	206×203×58	206	203	38	20	58	19.0
Trapezoidal	WPt 190	190×212.5×25	190	212.5	17	8	25	7.9
	WPt 241	241×290.5×30	241	290.5	22	8	30	19.5

 

Note: Studs Extra
If arc studs are required, please stipulate the size and position required.
Washers, Nuts, Studs, Threads,Holes are available.

Hunan Hyster Material Technology Co., LTD.

Hunan Hyster Material Technology Co., LTD. was founded in 1995, we are a professional manufacturer & exporter of composite Bi-metallic wear blocks/wear plates, Bimetallic wear pipes, Chocky bars, Wear buttons(CrMo white iron vacuum brazed onto a mild steel base plate, hardness 63HRC/700BHN), Chromium carbide overlay wear plates, Ni-hard wear Liners/Billets, and other wear castings for Mining, Quarrying, Construction and other heavy industries. We are located in New and High-Tech Development Zones of Changsha city, capital of Hunan province, middle of China.

Our annual output of bi-metallic wear blocks/bars/plates is more than 3000tons, capable to produce about 1200 different sizes and shapes; annual output of wear-resistant castings is more than 3000 tons, and hardfacing wear plates more than 2000 tons.