These are bi-metallic composites having 700 BHN hardness and available in various sizes and shapes, shredder hammer tips can be used in sugar or coal industry to do crushing and shredding performance, it has excellent impact and abrasion resistance properties & enhanced service life.
These shredder hammer tips are used as an alternative to conventional hardfacing in:
--Crusher mills
--Hammer mills
These hammers find application in
I) Sugar Industry
II) Mining & Mineral Processing Industry.
III) Cement & Steel Industry
TYPE 1 HAMMER TIPS: (FLAT TYPE)
Item No. |
Size(mm) |
N.W.(kg) |
| HC1 90-90 |
90x90x45 |
2.9 |
| HC1 90-50 |
90x50x45 |
1.6 |
| HC1 50-50 |
50x50x38 |
0.7 |
| HC1 80-80 |
80x80x45 |
2.4 |
| HC1 100-100 |
100x100x45 |
3.6 |
| HC1 64-64 |
64x64x40 |
1.2 |
| HC1 80-56 |
80x56x45 |
1.6 |
TYPE 2 HAMMER TIPS: (V TYPE)
Item No. |
Size(mm) |
N.W(kg) |
| HC2 90-90 |
90x90x50 |
3.0 |
| HC2 80-56 |
80x56x50 |
1.8 |
TYPE 3 HAMMER TIPS: (U TYPE)
Item No. |
Size(mm) |
N.W.(kg) |
| HC3 90-90 |
90x90x50 |
3.0 |
| HC3 90-50 |
90x50x55 |
1.8 |
| HC3 90-56 |
90x56x55 |
1.9 |
>Material,
ASTM A532 15/3 CrMo white iron casting , chemical composition ( percentage )
| C |
Cr |
Mo |
Si |
Mn |
Ni |
Cu |
P |
S |
| 2.0-3.3 |
14-18 |
≤ 3.0 |
≤ 1.5 |
≤ 2.0 |
≤ 2.5 |
≤ 1.2 |
≤ 0.1 |
≤ 0.06 |
Q235 mild steel backing , chemical composition ( percentage )
| C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Cu |
| 0.2 |
0.35 |
1.4 |
0.045 |
0.05 |
0.3 |
0.3 |
0.3 |
0.3 |
>Mechanical Property,
-Minimum Hardness, 700 HBN / 63 HRC
-Minimum Tensile Strength, 630Mpa.
-Minimum Shearing Strength, 250Mpa.
OTHER TYPICAL PRODUCTS AND SERVICE
-Wear plates, wear liners
-Chocky bars and wear buttons
-Wear blocks, wear bars
-Custom made wear liners
-Bucket repair and protection
-Full Fabrication services
-Sugar mill hammer tips
-Drilling, milling or machining
-Casting/Investment casting
-Fast service and timely delivery
Audited Supplier 