Wear Buttons Wear Protection and Wear Repair for Shovel Bucket Wear Product

• After-sales Service: Oversea
• Warranty: 90 Days
• Type: Crawler Excavator
• Usage: Special Excavator, Marine Excavator, Mining Excavator, GM Excavator
• Bucket: Shovel
• Transmission: Hydraulic Transmission
• Model NO.: WB90 WB115 WB150
• Drive Type: Internal Combustion Drive
• Bucket Capacity: >1.5m³
• Size: Large-Scale
• Certification: ISO9001: 2000
• Condition: New
• Transport Package: Polywood Pallet/Crate
• Specification: 90*17/10
• Trademark: OEM
• Origin: China
• HS Code: 84314991
• Production Capacity: 100 Tons/Month

Product Description

wear buttons wear protection and wear repair for shovel bucket wear product 

most of our customer are from Germany, American, Australia, Spain, as well as South  Africa. welcome to choose us - the most experienced manufacturer and exporter for laminite wear plates, domite chocky bars, chromium carbide wear blocks, grinder hammer tips, white iron wear bars as well as Cr-c overlay wear plate.

Laminated White Iron Wear Blocks combined very high wear resistant qualities of a high chrome cast iron (15/3CrMo, 700 BHN - 63 HRc) with a weldable & high impact toughness mild steel by Vacuum brazing furnace, which are exceptionally resistant to impact and abrasion while retaining.
 

Wear Button is a round shaped highly alloyed chromium white iron wear part. It's mainly used on the side plate of excavator. The hardness of this kind of wear part reaches HB700. The mild steel backing plate has very good welding performance while bearing high impact. The shear strenth of the bonding is over 200PMa and will not separate.
This product is very easy to use. 
It's easy to be cut and welded on curved surface without pre-heat or after heat treatment. 

 

It's easy to be transported as it's very small. 
It's an ideal samll area repairing wear part without too much welding time.
We have a complete range of specification and are able to customize and develop according to customer's requirement.
Comparing with normal High manganese steel wear resistant casting wear parts, this product's service life is 4-8 times longer.
 

Typical products,

Chocky bars Standard wear bars Knife edges

Wafer strips Wear buttons& donuts Skid bars

Wear plates Shredder hammer tips Shaped wear bars

 

overlay wear plates cutter tooth custom made products
 

CHEMICAL COMPOSITION

C	Cr	Mn	Mo	Cu	P	Si	S	B,V,Nb
2.5-3.5	15-18	0.5-1.0	0.5-2.5	0.5-1.0	0.02max	0.5-1.0	0.02max	0.1-0.5

 

 

THE MECHANICAL PROPERTY

 1) Tensile Strength 630 Mpa Min.

 2) Shearing Strength 250 Mpa Min.

 

 3) Hardness 63 HRC / 700 BHN