MaterialThis Bi-metallic wear resistant product, as a combination of high Chromium cast iron (ASTM A532 15/3CrMo, 700BHN - 63HRc) metallurgically bonded to a mild steel backing plate, obtains both very high abrasion resistance and weldability. Chemical Composition of White Iron
Mechanical Property of White Iron1. Tensile Strength: 630 MPa
2. Shearing Strength: 250 MPa
3. Hardness: 63 HRCMicro-Structure of White Iron Product SeriesChocky Bars Wear Buttons Wear DonutsStandard Wear Bars Micro-Ledges Wear PlatesRock Box Liners Skid Wear Bars Shaped Wear BarsWafer Strips Grizzly Bars Elbow Wear BarsShredder Hammer Tips Knife Edges Overlay Wear Plates ApplicationsWear Pads Jaw Crushers Chute Linings Ore ChutesCrusher Chutes Tripper Chutes Flop Gates Bucket LinersGrizzly Bars Lip Protectors Screen Plates Vibratory FeedersFloor Liners Loaders Wear Aprons Knife InsertsCrusher Bars Run Out Rolls Dump Hoppers Crusher HoppersSpecifications of Wafer Strips
The standard length of Wafer Strip is 240mm, with 12mm thickness in various widths from 25mm to 65mm. Customized grades and sizes are available as per the clients' specific need.With its standard thickness, Wafer Strip is an optimal selection for strict weight-increase limit and surface flatness requirement.
|Item No.||Size (mm)||Dimension (mm)||N.W. (kg)|
Hunan Hyster Material Technology Co., LTD.Founded in 1995, Hyster is a professional manufacturer & exporter of Bi-metallic Wear Blocks & Plates, Wear Pipes, Chocky Bars, Wear Buttons (white iron vacuum brazed onto mild steel, 63HRC/700BHN), Chromium Carbide Overlay Wear Plates, Ni-Hard Castings/Plates, Tungsten Carbide Castings for Mining, Quarrying, and other heavy industries.