WE ARE OEM FACTORY FOR FORDSTEEL CHILE, BYG SPAIN ,ASGCO,CAT,ESCO,ETC.
Laminated White Iron Wear Blocks combined very high wear resistant qualities of a high chrome cast iron (15/3CrMo, 700 BHN - 63 HRc) with a weldable & high impact toughness mild steel by Vacuum brazing furnace, which are exceptionally resistant to impact and abrasion while retaining.
High chromium wear-resistant casting wear parts is vacuum brazed by a highly alloyed chromium white iron and mild steel backing plate.The hardness of this kind of wear part reaches HB700. The mild steel backing plate has very good welding performance while bearing high impact. The shear strenth of the bonding is over 200PMa and will not separate.
This product is very easy to use.
It's easy to be cut and welded on curved surface without pre-heat or after heat treatment.
It's easy to be transported as it's very small.
It's an ideal samll area repairing wear part without too much welding time.
We have a complete range of specification and are able to customize and develop according to customer's requirement.
Comparing with normal High manganese steel wear resistant casting wear parts, this product's service life is 4-8 times longer.
Typical products,
Chocky bars Standard wear bars Knife edges
Wafer strips Wear buttons& donuts Skid bars
Wear plates Shredder hammer tips Shaped wear bars
overlay wear plates cutter tooth custom made products
CHEMICAL COMPOSITION
| C |
Cr |
Mn |
Mo |
Cu |
P |
Si |
S |
B,V,Nb |
| 2.5-3.5 |
15-18 |
0.5-1.0 |
0.5-2.5 |
0.5-1.0 |
0.02max |
0.5-1.0 |
0.02max |
0.1-0.5
|
THE MECHANICAL PROPERTY
1) Tensile Strength 630 Mpa Min.
2) Shearing Strength 250 Mpa Min.
3) Hardness 63 HRC / 700 BH