OEM White Iron Grinder Tips for Hammer Crusher (DLP653)

• Customization: Available
• Type: White Iron
• Shape: Flat,V,U
• Model NO.: DLP653, DLP1654, DLP1927, DLP2039
• Name: White Iron Grinder Tips
• Rockwell Hardness: 63HRC
• Brinell Hardness: 700bhn
• Technology: Vacuum Brazing
• Types: Falt,V,U
• Transport Package: Polywood Pallet and Crate
• Specification: TOP GRADE
• Trademark: HYSTER, OEM, CQMS, DOMITE
• Origin: Changsha, Hunan, Cn
• HS Code: 8479909090
• Production Capacity: 80 Tons Per Month

Product Description

HYSTER has been an independent international supply, design and engineering company, since 1995. 

welcome to choose us - the most experienced manufacturer and exporter for laminite wear plates(ASTM A532 chromium carbide white iron & mild steel backing plate, 63HRC-700BHN), domite chocky bars, chromium carbide wear blocks, grinder hammer tips, white iron wear bars as well as Cr-c overlay wear plate.



These are bi-metallic composites having 700 BHN hardness and available in various sizes and shapes, shredder hammer tips can be used in sugar or coal industry to do crushing and shredding performance, it has excellent impact and abrasion resistance properties & enhanced service life.

These shredder hammer tips are used as an alternative to conventional hardfacing in:
--Crusher mills
--Hammer mills

These hammers find application in
  I) Sugar Industry
  II) Mining & Mineral Processing Industry.
  III) Cement & Steel Industry

TYPE 1 HAMMER TIPS: (FLAT TYPE)

Item No.	Size(mm)	N.W.(kg)
HC1 90-90	90x90x45	2.9
HC1 90-50	90x50x45	1.6
HC1 50-50	50x50x38	0.7
HC1 80-80	80x80x45	2.4
HC1 100-100	100x100x45	3.6
HC1 64-64	64x64x40	1.2
HC1 80-56	80x56x45	1.6

TYPE 2 HAMMER TIPS: (V TYPE)

Item No.	Size(mm)	N.W(kg)
HC2 90-90	90x90x50	3.0
HC2 80-56	80x56x50	1.8

TYPE 3 HAMMER TIPS: (U TYPE)

Item No.	Size(mm)	N.W.(kg)
HC3 90-90	90x90x50	3.0
HC3 90-50	90x50x55	1.8
HC3 90-56	90x56x55	1.9

>Material,
ASTM A532 15/3 CrMo white iron casting , chemical composition ( percentage )

C	Cr	Mo	Si	Mn	Ni	Cu	P	S
2.0-3.3	14-18	≤ 3.0	≤ 1.5	≤ 2.0	≤ 2.5	≤ 1.2	≤ 0.1	≤ 0.06

 
Q235 mild steel backing , chemical composition ( percentage )

C	Si	Mn	P	S	Cr	Ni	Mo	Cu
0.2	0.35	1.4	0.045	0.05	0.3	0.3	0.3	0.3

 
>Mechanical Property,
-Minimum Hardness, 700 HBN / 63 HRC
-Minimum Tensile Strength, 630Mpa.
-Minimum Shearing Strength, 250Mpa.



OTHER TYPICAL PRODUCTS AND SERVICE
-Wear plates, wear liners
-Chocky bars and wear buttons
-Wear blocks, wear bars
-Custom made wear liners
-Bucket repair and protection
-Full Fabrication services
-Sugar mill hammer tips
-Drilling, milling or machining
-Casting/Investment casting
-Fast service and timely delivery