• Bimetallic Chocky Bars for Excavator Loaders Buckets Bimetallic Chockblock
  • Bimetallic Chocky Bars for Excavator Loaders Buckets Bimetallic Chockblock

Bimetallic Chocky Bars for Excavator Loaders Buckets Bimetallic Chockblock

Certification: ISO 9001:2000
Standard: ASTM
Surface Treatment: Polishing
Manufacturing Process: Casting
Material: Cast Iron
Name: Buckets Bimetallic Chockblock
Customization:

Contact Supplier

Ms. Shing Xiao
Technical Commercial Manager
Gold Member Since 2015

Suppliers with verified business licenses

Manufacturer/Factory & Trading Company

Basic Info.

Model NO.
CB25. CB40, CB50, CB65, CB80, CB90, CB100, CB130.
Materials
High Chrome Cast Iron&Mild Ste
Hardness
63HRC
Technology
Vacuum Brazing
Transport Package
Oli Film, Poly-Wood Crate, Pallets
Specification
High Grade
Trademark
Hyster, OEM, Domite, Duablock, vidablock
Origin
China Hunan
HS Code
84314991
Production Capacity
80tons/Month

Product Description

buckets bimetallic chockblock

Laminated white iron Wear buttons are unique wear resistant materials in that they combine very high wear resistant qualities of a high chrome cast iron (15/3CrMo, 700 BHN - 63 HRC) with a weldable & high impact toughness mild steel through a metallurgical bond to create a product that is exceptionally resistant to impact and abrasion while retaining.


Very easy to use, no pre or post heating when welding. Available in diameters from 60mm up to 150mm. Develop your own layout and pattern to suit your particular wear protection solution.

Dome&Flat Shaped Round: Perfect solution for ground engaging applications as on adaptor teech, shovels, buckets, heavy earth moving equipment etc. Can well use them in conjunction with Chocky Bars, Wear Plates or individually to provide protection or security under the toughest impact and wear abrasion circumstances.

Types:

ITEM
SIZE(mm)Net weight(kg)
WB6060x270.7
WB7575x270.8
WB9090x271.4
WB110110x322.1
WB115115x322.5
WB150150x415.7


Please contact us if you would like other sizes if needed.

>Material,
ASTM A532 15/3 CrMo white iron casting , chemical composition ( percentage )

C
CrMoSiMnNiCuPS
2.0-3.314-18≤ 3.0≤ 1.5≤ 2.0≤ 2.5≤ 1.2≤ 0.1≤ 0.06

 
Q235 mild steel backing , chemical composition ( percentage )

C
SiMnPSCrNiMoCu
0.20.351.40.0450.050.30.30.30.3

 
>Mechanical Property,
-Minimum Hardness, 700 HBN / 63 HRC
-Minimum Tensile Strength, 630Mpa.
-Minimum Shearing Strength, 250Mpa.


 

Send your message to this supplier

*From:
*To:
avatar Ms. Shing Xiao
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Contact Supplier

Ms. Shing Xiao
Technical Commercial Manager
Gold Member Since 2015

Suppliers with verified business licenses

Manufacturer/Factory & Trading Company
Number of Employees
26
Year of Establishment
2013-10-21